Studiu asupra microstructurii și proprietăților mecanice ale îmbinării sudate cu laser din aliaj de titan Ti-6Al-4V de 1,5 mm

Cuvinte cheie:Aliaj de titan Ti-6Al-4V/ sudare cu laser / microstructură / proprietăți mecanice

Autori: Fu Heguo, Liu Guangxin, Xie Hongzhi, Jiang Wentong etc

Shenyang Aircraft Industry Group Co., Ltd

Sursa: sudare si taiere

Rezumat: experimentul sudării cu laser plus sudarea prin modificarea suprafeței de 1,5 mmAliaj de titan Ti-6Al-4V was carried out, and the microstructure and static properties of the joint were observed. The results show that due to the influence of different welding thermal cycles, The structure area of laser welding plus surface modification welding joint can be divided into a base metal area, heat affected area, equiaxed crystal area at the bottom of weld, and columnar crystal area at the top of the weld, there is widmanstatten structure in the weld structure, With the increase of the distance from the fusion line, the microstructure of the heat-affected zone increases ' The volume fraction decreased gradually.

Proprietățile mecanice ale îmbinării arată că rezistența la tracțiune și rezistența la forfecare sunt echivalente cu metalul de bază, iar unghiul minim de îndoire este de 35 de grade, ceea ce indică faptul că îmbinarea poate fi aplicată în inginerie.

Morfologia îmbinării sudate din aliaj de titan Ti-6Al-4V

Microstructura zonei de sudare

Morfologia microstructurii diferitelor regiuni din zona afectată de căldură

Valoarea de testare a proprietăților mecanice ale îmbinării

Valoarea medie a proprietăților mecanice ale îmbinării